Anodic Behaviour of Ti-12 in Various Electrolytes


Affiliations
1 Department of Chemistry, University College of Engineering, Osmania University, Hyderabad-500007, Telangana, India
     

   Subscribe/Renew Journal


Anodization of Ti-12 alloy has been carried out in various electrolytes at different constant current densities and temperatures. Kinetics of anodic films was studied in different electrolytes at different constant current densities ranging from 4mAcm-2 to 64mAcm-2 and at different temperatures ranging from 298 to 338K. From the plots of formation voltage (V) vs time (t), rates of formation were calculated. The rate of film formation and breakdown voltage increase with increase in constant current density while decrease with increase in temperature. The kinetics were found better in sulphamic acid electrolyte at room temperature compared to other electrolytes at the same anodizing conditions.

Keywords

Anodization, Constant Current Density, Formation Rate, Titanium-12.
Subscription Login to verify subscription
User
Notifications
Font Size


  • D. M. Brunette, P. Tengavall, M. Textor and P. Thomsen, Springer, 171 (2001).

  • H. Luckey, and F. Kubli, ASTM, 796 (1981).

  • G. R. Parr, L. K. Gardner, and R. W. Toth, J. Posthent. Dent., 54, 410 (1985). https://doi.org/10.1016/00223913(85)90562-1

  • J. E. G. Gonzalez and J. C. Minza-Rosca, J. Electroanal. Chem., 471, 109 (1999). https://doi.org/10.1016/S00220728(99)00260-0

  • K. S. Brammer, C. J. Frandsen and S. Jin, Trends Biotechnol., 30, 315 (2012). https://doi.org/10.1016/j.tibtech.2012.02.005 PMid:22424819

  • S. L. De-Assis, S. W. Solynec and I. Costa, Electrochim. Acta., 51, 1815 (2006). https://doi.org/10.1016/j.electacta.2005.02.121

  • F. H. Jones, Surf. Sci. Rep., 42, 75 (2001). https://doi.org/10.1016/S0167-5729(00)00011-X

  • R. Narayanan, H. J. Lee, J. Y. Kwon and K. H. Kim, Mater. Chem. Phys., 125, 510 (2001). https://doi.org/10.1016/j.matchemphys.2010.10.024

  • G. K. Mor, O. K. Varghese, M. Paulose, K. Shankar, and C. A. Grimes, Sol. Energ. Mater. Sol. Cell., 90, 2011 (2006). https://doi.org/10.1016/j.solmat.2006.04.007

  • Z. M. Yan, T. W. Guo, H. B. Pan and J. J. Yu, Mater. Trans., 43, 3142 (2002). https://doi.org/10.2320/matertrans.43.3142

  • M. V. Diamanti, B. Del Curto, C. Passaro and M. P. Pedeferri, Color. Res. Appl., 37, 384 (2012). https://doi.org/10.1002/ col.20683

  • M. Kisaichi, Surf. Technol., 40, 66 (1989).

  • B. B. Secley, Metal. Progress, 9, 35 (1982).

  • R. S. Hyam, and D. Choi, RSC ADV., 3, 7057 (2013). https://doi.org/10.1039/c3ra40581h

  • V. Jeevana Jyothi, and Ch. Anjaneyulu, E J. Chem., 6, 880 (2009). https://doi.org/10.1155/2009/579860

  • Ch. Anjaneyulu, Thesis, Osmania University, 1981.

  • G. Raghunathreddy, A. Lavanya and Ch. Anjaneyulu, Bull. Electrochem., 22, 235 (2006).

  • P. Baskar Reddy and A. Panasa Reddy, Bull. Electrochem., 19, 481 (2003).

  • T. Aerts, Th. Dimogerontakis, I. D. Graeve, J. Fransaer and H.Terryn, Surf. Coating. Tech., 201, 7310 (2007). https://doi.org/10.1016/j.surfcoat.2007.01.044

  • P. Michal, A. Vagaska, E. Fechova, M. Gombar and D. Kozak, METABK, 55, 403 (2016).


Abstract Views: 382

PDF Views: 3




  • Anodic Behaviour of Ti-12 in Various Electrolytes

Abstract Views: 382  |  PDF Views: 3

Authors

U. Raghavender
Department of Chemistry, University College of Engineering, Osmania University, Hyderabad-500007, Telangana, India
K. Vijay Kumar
Department of Chemistry, University College of Engineering, Osmania University, Hyderabad-500007, Telangana, India
E. Rajasheker Reddy
Department of Chemistry, University College of Engineering, Osmania University, Hyderabad-500007, Telangana, India
A. Panasa Reddy
Department of Chemistry, University College of Engineering, Osmania University, Hyderabad-500007, Telangana, India

Abstract


Anodization of Ti-12 alloy has been carried out in various electrolytes at different constant current densities and temperatures. Kinetics of anodic films was studied in different electrolytes at different constant current densities ranging from 4mAcm-2 to 64mAcm-2 and at different temperatures ranging from 298 to 338K. From the plots of formation voltage (V) vs time (t), rates of formation were calculated. The rate of film formation and breakdown voltage increase with increase in constant current density while decrease with increase in temperature. The kinetics were found better in sulphamic acid electrolyte at room temperature compared to other electrolytes at the same anodizing conditions.

Keywords


Anodization, Constant Current Density, Formation Rate, Titanium-12.

References





DOI: https://doi.org/10.18311/jsst%2F2018%2F16027